序号
Number
试验项目
Experiment Items
试验方法和条件
Experiment Method And Conditions
参考
Reference
1 耐焊接热
Solder Resistance
260℃+5℃ for 10+2sec.
Immerse body into solder 1/16"+1/32"
MIL-STD-750D
METHOD-2031.2
2 可焊性
Solderability
230℃+5℃ for 5 sec. MIL-STD-750D
METHOD-2026.10
3 拉力测试
Pull Test
1kg in Axial Lead Direction for 10 sec. MIL-STD-750D
METHOD-2036.4
4 弯曲测试
Bend Test
0.5kg Weight Applied To Each Lead
Bending Arcs 90 ±5℃  For Three Times
MIL-STD-750D
METHOD-2036.4
5 高温反偏
High Temperature
Reverse Bias Test
TA=100℃ for 1000 Hrs at VR=80% Rated VR MIL-STD-750D
METHOD-1038.4
6 正向寿命
Forward Operation Life Test
TA=25℃ Rated Average Rectified Current
for 500 Hrs
MIL-STD-750D
METHOD-1027.3
7 间隙寿命
Intermittent Operation  Life
On state:5 min Tj=125℃-175℃ with
Rated IRMS Power.
Off state:5 min Tj=TA+15℃ With
Cool Forced Air.On and Off for 1000 Cycles.
MIL-STD-750D
METHOD-1036.3
8 高温蒸煮
Pressure Cooker
15 PSIG,TA=121℃,24hrs MIL-STD-750D
9 高温循环
Temperature Cycling
-55℃/+125℃ 30 Minutes For Dwelled Time
5 Minutes For Transfered Time.
Total 10 Cycles.
MIL-STD-750D
METHOD-1051.7
10 冲击
Thermal Shock
0℃ for 5 min,100℃ for 5Min,Total 10 Cycles MIL-STD-750D
METHOD-1056.7
11 正向浪涌
Forward Surge
8.3 ms Single Hale Sine-wave Superimposed
On Rated Load, One Surge.
MIL-STD-750D
METHOD-4066.4
12 高温高射
Humidity Test
TA=65℃,RH=98% for 1000hrs. MIL-STD-750D
METHOD-1021.3
13 高温存炉
High Temperature Storage Life
150℃ for 1000 Hrs MIL-STD-750D
METHOD-1031.5